アルミナジルコニアブラストメディア ZA40

ZA25およびZA40ジルコニア溶融アルミナは、高度な溶融プロセスで製造され、従来のサンドブラスト媒体よりも耐用年数が3～6倍長く、粒子の埋め込みや廃棄物処理の必要性を大幅に削減できます。ZA25は切削力が強く、重研磨、スケール除去、高圧サンドブラスト装置に適しています。ZA40は靭性と耐久性が高く、高精度加工や高い表面仕上げが要求される用途、特に低圧サンドブラスト装置に適しています。

製品について

MIL-P-85891Aに準拠

製品リスト

詳細はこちら

| 特徴

| 特徴

  • Extremely high durability.
  • Provide uniform surface texture and matte finish.
  • Reduced media breakdown improves cleanliness and reduces contamination risk.
  • Suitable for a wider range of materials, including sensitive ones.
  • High toughness, but less aggressive than ZA25.
  • Compatible with a wide range of blasting systems, including pneumatic and turbine equipment.
• Extremely high durability.
• Provide uniform surface texture and matte finish.
• Reduced media breakdown improves cleanliness and reduces contamination risk.
• Suitable for a wider range of materials, including sensitive ones.
• High toughness, but less aggressive than ZA25.
• Compatible with a wide range of blasting systems, including pneumatic and turbine equipment.
ZA40アルミナジルコニアブラストメディア
代表値 ZrO₂ Al₂O₃ その他
% 40 60 <1
項目 ZA40
比重 4.60g/cm³
かさ密度（LPD） 2.15-2.45g/cm³
ビッカー硬度（100g荷重） 19 GPa
融点 1900°C
粒子形状 単斜晶正方晶
化学的性質 両性具有
酸およびアルカリとの反応 ノー
最高使用温度 1600°C
クリスタルサイズ ≤20um
炭素との反応 1650℃からカーバイドを形成
カラー グレー
比熱容量（cal/g-C） 0.2205 (50-500°C)
熱伝導率 0.2718 cal/cm²-sec-°C
Linear Expansivity (X10⁻⁶) 6.82 (100-700°C)
ZA40アルミナジルコニアブラストメディア
代表値 ZrO₂ Al₂O₃ その他
% 40 60 <1
項目 ZA40
比重 4.60g/cm³
かさ密度（LPD） 2.15-2.45g/cm³
ビッカー硬度（100g荷重） 19 GPa
融点 1900°C
粒子形状 単斜晶正方晶
化学的性質 両性具有
酸およびアルカリとの反応 ノー
最高使用温度 1600°C
クリスタルサイズ ≤20um
炭素との反応 1650℃からカーバイドを形成
カラー グレー
比熱容量（cal/g-C） 0.2205 (50-500°C)
熱伝導率 0.2718 cal/cm²-sec-°C
線膨張率 (X10-6) 6.82 (100-700°C)
Fサンド g/cm³ Fサンド g/cm³ Fサンド g/cm³
F22 2.12–2.18 F24 2.09–2.15 F30 2.00–2.12
F54 1.92–2.03 F60 1.93–2.00 F70 1.88–2.01
F120 1.84–1.95 F150 1.83–1.95 F180 1.81–1.93
F36 1.99–2.10 F40 1.96–2.08 F46 1.94–2.05
F80 1.88–1.98 F90 1.86–2.00 F100 1.85–1.97
F220 1.82–1.92
Fサンド g/cm³ Fサンド g/cm³ Fサンド g/cm³
F22 2.12–2.18 F24 2.09–2.15 F30 2.00–2.12
F54 1.92–2.03 F60 1.93–2.00 F70 1.88–2.01
F120 1.84–1.95 F150 1.83–1.95 F180 1.81–1.93
F36 1.99–2.10 F40 1.96–2.08 F46 1.94–2.05
F80 1.88–1.98 F90 1.86–2.00 F100 1.85–1.97
F220 1.82–1.92

| アプリケーション

| アプリケーション

  • Polishing composite floors;
  • Grinding composite stainless steel;
  • Providing a matte uniform surface for implants, surgical tools, etc;
  • Cleaning and finishing sensitive electronic components;
  • Surface profiling of aluminum or composite materials;
  • Achieving a smooth, consistent finish on tools and molds.
• Polishing composite floors;
• Grinding composite stainless steel;
• Providing a matte uniform surface for implants, surgical tools, etc;
• Cleaning and finishing sensitive electronic components;
• Surface profiling of aluminum or composite materials;
• Achieving a smooth, consistent finish on tools and molds.

━━ 関連コンテンツ

サンドブラストは健康被害で禁止されている？ 真実と概要

クライオジェニック・デフラッシング・プロセスとは何ですか？

タイプIIIメラミン効率的な剥離と精密洗浄

━━ その他の製品

イットリア安定化ジルコニアビーズ (YZ)

イットリア安定化ジルコニアビーズ（YZ）は、安定化酸化ジルコニウム材料で作られた高密度、高硬度の微細セラミックビーズです。

アルミナジルコニアブラストメディア ZA40

ZA25およびZA40ジルコニア溶融アルミナは、高度な溶融プロセスで製造されています。

アルミナジルコニアブラストメディア

ZA25およびZA40ジルコニア溶融アルミナは、高度な溶融プロセスで製造されています。