Why Ceramic Polishing Media Grades Matter
Improper grade selection is the most common cause of polishing defects such as surface haze, inconsistent gloss, or excessive cycle times. Ceramic polishing media grades are designed to operate within defined aggressiveness windows. Selecting a grade outside its intended Ra range often leads to diminishing returns rather than faster polishing.
This page should be used in conjunction with the Ceramic Polishing Media pillar as a decision-support reference.
Engineering Basis for Grade Classification
Ceramic polishing media grades are not determined by shape alone but by a combination of internal and physical parameters.
| Classification Parameter | Function in Polishing |
|---|---|
| Abrasive grain size | Defines surface refinement capability |
| Abrasive content (wt%) | Controls polishing aggressiveness |
| Насыпная плотность | Determines impact energy |
| Porosity | Maintains slurry circulation and consistency |
Overview of Ceramic Polishing Media Grades
| Grade | Typical Abrasive Size | Насыпная плотность | Target Ra Range | Primary Function |
|---|---|---|---|---|
| Medium Polishing | F400–F600 | 2.0–2.2 g/cm³ | Ra 1.0–1.2 µm | Surface smoothing after deburring |
| Fine Polishing | F600–F800 | 1.8–2.0 g/cm³ | Ra 0.6–0.8 µm | Cosmetic refinement |
| Ultra-Fine Polishing | F800–F1000 | 1.7–1.9 g/cm³ | Ra 0.4–0.6 µm | High-gloss preparation |
Expected Ra outcomes should always be verified against process conditions using the Ceramic Polishing Media Ra Chart.
Medium Polishing Grade
Medium polishing ceramic media represents the transition stage between deburring and fine surface refinement. It is commonly used as the first polishing step following ceramic tumbling or aggressive deburring.
| Abrasive grain size | F400–F600 |
| Abrasive content | 6–10 wt% |
| Насыпная плотность | 2.0–2.2 g/cm³ |
| Typical cycle time | 60–120 minutes |
| Achievable Ra | Ra 1.0–1.2 µm |
Medium polishing grades are suitable for aluminum alloys, carbon steel, and stainless steel parts that still show visible machining or tumbling marks.
Fine Polishing Grade
Fine polishing ceramic media is the most widely used grade in cosmetic mass finishing. It balances surface refinement speed with dimensional safety and is commonly applied before anodizing or coating processes.
| Abrasive grain size | F600–F800 |
| Abrasive content | 4–7 wt% |
| Насыпная плотность | 1.8–2.0 g/cm³ |
| Typical cycle time | 90–180 minutes |
| Achievable Ra | Ra 0.6–0.8 µm |
This grade is particularly effective for aluminum components requiring uniform matte or satin finishes. Application-specific guidance is available in Ceramic Polishing Media for Aluminum.
Ultra-Fine Polishing Grade
Ultra-fine polishing ceramic media is designed for applications where surface quality is the dominant requirement. Material removal is minimal, and polishing efficiency depends on extended cycle time and stable process control.
| Abrasive grain size | F800–F1000 |
| Abrasive content | 3–5 wt% |
| Насыпная плотность | 1.7–1.9 g/cm³ |
| Typical cycle time | 120–240 minutes |
| Achievable Ra | Ra 0.4–0.6 µm |
This grade is typically used for stainless steel, decorative components, and high-visibility consumer or industrial parts.
Grade Selection Logic Based on Surface Targets
| Initial Condition | Target Ra | Recommended Grade |
|---|---|---|
| Post-machining surface | >1.0 µm | Medium polishing |
| Pre-anodizing aluminum | 0.6–0.8 µm | Fine polishing |
| High cosmetic requirement | <0.6 µm | Ultra-fine polishing |
Material compatibility and density constraints should be evaluated together with the Ra performance chart.
Common Grade Selection Mistakes
- Using ultra-fine grades to remove machining marks
- Over-polishing thin aluminum parts with high-density media
- Ignoring media density when processing delicate geometries
- Expecting Ra improvement beyond grade capability
Ceramic vs Plastic Polishing Media in Grade Selection
In some applications, plastic polishing media may appear interchangeable with ceramic polishing grades. However, ceramic media offers superior Ra predictability and service life. A detailed comparison is available in Ceramic vs Plastic Polishing Media.
Request Grade Recommendation
If you are unsure which ceramic polishing media grade fits your application, provide your material type, initial surface condition, target Ra, and machine type. Our technical team can recommend the optimal grade and process window.