{"id":13733,"date":"2026-07-23T05:52:19","date_gmt":"2026-07-23T05:52:19","guid":{"rendered":"https:\/\/hlh-js.com\/?p=13733"},"modified":"2026-07-23T05:52:19","modified_gmt":"2026-07-23T05:52:19","slug":"shot-peening-3d-printed-metal-parts-improving-fatigue-life-with-compressive-residual-stress","status":"publish","type":"post","link":"https:\/\/hlh-js.com\/es\/resource\/blog\/shot-peening-3d-printed-metal-parts-improving-fatigue-life-with-compressive-residual-stress\/","title":{"rendered":"Shot Peening 3D Printed Metal Parts: Improving Fatigue Life with Compressive Residual Stress"},"content":{"rendered":"<div class=\"hlh-3dp-c10\">\n<style>\n.hlh-3dp-c10{font-family:'Inter',-apple-system,BlinkMacSystemFont,'Segoe UI',Roboto,sans-serif;color:#374151;line-height:1.78;max-width:860px;margin:0 auto;padding:0;font-size:16px}\n.hlh-3dp-c10 *,.hlh-3dp-c10 *::before,.hlh-3dp-c10 *::after{box-sizing:border-box}\n.hlh-3dp-c10 h1{font-size:2rem;font-weight:800;color:#1a3456;line-height:1.22;margin:0 0 1rem;letter-spacing:-.025em}\n.hlh-3dp-c10 h2{font-size:1.42rem;font-weight:700;color:#1a3456;margin:2.5rem 0 .85rem;padding-bottom:.5rem;border-bottom:2px solid #e5e7eb}\n.hlh-3dp-c10 h3{font-size:1.1rem;font-weight:700;color:#1a3456;margin:1.75rem 0 .6rem}\n.hlh-3dp-c10 p{margin:0 0 1.05rem}\n.hlh-3dp-c10 a{color:#3730A3;text-decoration:none;border-bottom:1px solid #3730A355;transition:border-color .2s,color .2s}\n.hlh-3dp-c10 a:hover{border-bottom-color:#3730A3}\n.hlh-3dp-c10 ul,.hlh-3dp-c10 ol{padding-left:1.55rem;margin:0 0 1.05rem}\n.hlh-3dp-c10 li{margin-bottom:.45rem}\n.hlh-3dp-c10 strong{color:#1a3456;font-weight:700}\n.hlh-3dp-c10-meta{display:flex;flex-wrap:wrap;gap:.4rem 1.3rem;font-size:.83rem;color:#6b7280;margin-bottom:1.4rem;padding-bottom:.85rem;border-bottom:1px solid #e5e7eb}\n.hlh-3dp-c10-intro{font-size:1.04rem;color:#4b5563;line-height:1.8;margin-bottom:1.9rem;padding:1rem 1.25rem;background:#f8fafc;border-left:4px solid #3730A3;border-radius:0 8px 8px 0}\n.hlh-3dp-c10-back{font-size:.85rem;color:#6b7280;margin-bottom:1.5rem;padding:.65rem 1rem;background:#f0f4f8;border-radius:6px}\n.hlh-3dp-c10-back a{color:#3730A3}\n.hlh-3dp-c10-toc{background:#f0f4f8;border:1px solid #d1dce8;border-left:4px solid #3730A3;border-radius:0 10px 10px 0;padding:1.15rem 1.4rem 1.25rem;margin:0 0 2.3rem}\n.hlh-3dp-c10-toc-title{font-weight:800;color:#1a3456;font-size:.8rem;margin:0 0 .75rem;text-transform:uppercase;letter-spacing:.1em}\n.hlh-3dp-c10-toc ol{margin:0;padding-left:1.25rem}\n.hlh-3dp-c10-toc li{margin-bottom:.32rem;font-size:.88rem}\n.hlh-3dp-c10-toc a{color:#1a3456;border-bottom:none;font-weight:500}\n.hlh-3dp-c10-toc a:hover{color:#3730A3}\n.hlh-3dp-c10-tw{overflow-x:auto;margin:1.25rem 0 1.4rem;border-radius:8px;border:1px solid #e5e7eb}\n.hlh-3dp-c10 table{width:100%;border-collapse:collapse;font-size:.845rem}\n.hlh-3dp-c10 thead th{background:#1a3456;color:#fff;padding:.6rem .85rem;text-align:left;font-weight:600;font-size:.81rem;white-space:nowrap}\n.hlh-3dp-c10 tbody tr:nth-child(even){background:#f8fafc}\n.hlh-3dp-c10 tbody tr:hover{background:#f0f4f8}\n.hlh-3dp-c10 tbody td{padding:.55rem .85rem;border-bottom:1px solid #e5e7eb;vertical-align:top;line-height:1.5}\n.hlh-3dp-c10 tbody tr:last-child td{border-bottom:none}\n.hlh-3dp-c10-note{background:#fff8f0;border-left:4px solid #3730A3;border-radius:0 8px 8px 0;padding:.9rem 1.2rem;margin:1.4rem 0}\n.hlh-3dp-c10-note .nl{font-size:.7rem;font-weight:700;text-transform:uppercase;letter-spacing:.08em;color:#3730A3;margin-bottom:.3rem}\n.hlh-3dp-c10-note p{margin:0;font-size:.93rem}\n.hlh-3dp-c10-stats{display:grid;grid-template-columns:repeat(auto-fit,minmax(148px,1fr));gap:.8rem;margin:1.4rem 0}\n.hlh-3dp-c10-stat{background:#1a3456;color:#fff;border-radius:10px;padding:1rem;text-align:center}\n.hlh-3dp-c10-stat .sv{font-size:1.75rem;font-weight:800;color:#f0a830;line-height:1;margin-bottom:.28rem}\n.hlh-3dp-c10-stat .sl{font-size:.74rem;color:rgba(255,255,255,.8);line-height:1.3}\n.hlh-3dp-c10-steps{list-style:none;padding:0;margin:.7rem 0 1.25rem;counter-reset:st}\n.hlh-3dp-c10-steps li{counter-increment:st;display:flex;gap:.85rem;margin-bottom:.85rem;align-items:flex-start}\n.hlh-3dp-c10-steps li::before{content:counter(st);flex-shrink:0;width:1.9rem;height:1.9rem;background:#3730A3;color:#fff;border-radius:50%;display:flex;align-items:center;justify-content:center;font-weight:700;font-size:.8rem;margin-top:.1rem}\n.hlh-3dp-c10-faq{margin:0 0 2rem}\n.hlh-3dp-c10-fi{border:1px solid #e5e7eb;border-radius:8px;margin-bottom:.55rem;overflow:hidden}\n.hlh-3dp-c10-fi summary{padding:.85rem 1.1rem;font-weight:700;font-size:.92rem;color:#1a3456;cursor:pointer;list-style:none;display:flex;justify-content:space-between;align-items:center;background:#f8fafc}\n.hlh-3dp-c10-fi summary::-webkit-details-marker{display:none}\n.hlh-3dp-c10-fi summary::after{content:'+';font-size:1.2rem;color:#3730A3;flex-shrink:0;margin-left:1rem;font-weight:400}\n.hlh-3dp-c10-fi[open] summary::after{content:'\u2212'}\n.hlh-3dp-c10-fi[open] summary{background:#fff;border-bottom:1px solid #e5e7eb}\n.hlh-3dp-c10-fa{padding:.95rem 1.1rem;color:#374151}\n.hlh-3dp-c10-fa p{margin:0 0 .65rem}\n.hlh-3dp-c10-fa p:last-child{margin:0}\n.hlh-3dp-c10-cta{background:#1a3456;border-radius:14px;padding:1.9rem 1.85rem;text-align:center;color:#fff;margin:2.3rem 0 .9rem}\n.hlh-3dp-c10-cta h2{color:#fff;border:none;padding:0;margin:0 0 .65rem;font-size:1.35rem}\n.hlh-3dp-c10-cta p{color:rgba(255,255,255,.85);margin:0 0 1.2rem}\n.hlh-3dp-c10 a.hlh-3dp-c10-btn{display:inline-block;background:#3730A3;color:#fff !important;font-weight:700;padding:.75rem 2rem;border-radius:6px;text-decoration:none;font-size:.93rem;border:none;border-bottom:none !important;transition:background .2s}\n.hlh-3dp-c10 a.hlh-3dp-c10-btn:hover{opacity:.9;color:#fff !important;border-bottom:none !important}\n.hlh-3dp-c10-badge{display:inline-flex;align-items:center;background:#e8f0f8;color:#1a3456;font-size:.7rem;font-weight:700;padding:.2rem .6rem;border-radius:4px;text-transform:uppercase;letter-spacing:.05em;margin-bottom:.6rem}\nhr.hlh-3dp-c10-div{border:none;border-top:1px solid #e5e7eb;margin:2rem 0}\n<\/style><script type=\"application\/ld+json\">{\n    \"@context\": \"https:\\\/\\\/schema.org\",\n    \"@type\": \"Article\",\n    \"headline\": \"Shot Peening 3D Printed Metal Parts: Improving Fatigue Life with Compressive Residual Stress\",\n    \"description\": \"Complete guide to shot peening 3D printed metal parts for fatigue life improvement: Almen intensity specification, media selection, compressive residual stress mechanisms, and NADCAP compliance.\",\n    \"datePublished\": \"2026-07-01\",\n    \"dateModified\": \"2026-07-01\",\n    \"author\": {\n        \"@type\": \"Organization\",\n        \"name\": \"Jiangsu Henglihong Technology Co., Ltd.\",\n        \"url\": \"https:\\\/\\\/hlh-js.com\"\n    },\n    \"publisher\": {\n        \"@type\": \"Organization\",\n        \"name\": \"Jiangsu Henglihong Technology Co., Ltd.\",\n        \"url\": \"https:\\\/\\\/hlh-js.com\"\n    },\n    \"mainEntityOfPage\": {\n        \"@type\": \"WebPage\",\n        \"@id\": \"https:\\\/\\\/hlh-js.com\\\/resource\\\/blog\\\/shot-peening-3d-printed-metal-parts-improving-fatigue-life-with-compressive-residual-stress\\\/\"\n    },\n    \"keywords\": \"shot peening additive manufacturing, shot peening 3d printed metal parts, fatigue life 3d printing, compressive residual stress AM parts\"\n}<\/script><script type=\"application\/ld+json\">{\n    \"@context\": \"https:\\\/\\\/schema.org\",\n    \"@type\": \"FAQPage\",\n    \"mainEntity\": [\n        {\n            \"@type\": \"Question\",\n            \"name\": \"What is the difference between shot peening and bead blasting?\",\n            \"acceptedAnswer\": {\n                \"@type\": \"Answer\",\n                \"text\": \"Both use spherical media propelled at a surface, but differ fundamentally in purpose and control. Bead blasting is a surface conditioning and cleaning process \\u2014 fine glass beads at material-matched pressures reduce Ra, remove oxide, and create a uniform matte finish. No intensity specification is required. Shot peening is a precision engineering process \\u2014 harder, denser media at intensities measured with Almen test strips introduce a specific level of compressive residual stress at a quantified depth. Shot peening is always specified by Almen intensity, coverage percentage, and media type; bead blasting is specified by media mesh size and pressure only. In aerospace production, the two are sequential: bead blasting normalises the surface to the pre-peen Ra, then shot peening applies the Almen-specified intensity.\"\n            }\n        },\n        {\n            \"@type\": \"Question\",\n            \"name\": \"What Almen intensity should I specify for shot peening SLM Ti-6Al-4V?\",\n            \"acceptedAnswer\": {\n                \"@type\": \"Answer\",\n                \"text\": \"For SLM Ti-6Al-4V, typical Almen A intensities range from 0.008 to 0.015 inch arc height for thin sections (wall thickness below 3 mm) and 0.012 to 0.025 inch for heavier sections. These are broad guidelines; the specific Almen intensity for a production part must come from a fatigue optimisation study or from the design stress analysis. Higher intensity introduces deeper CRS but also higher surface Ra and greater cold-working, which can reduce ductility in thin walls. The optimum balances CRS depth against surface roughness increase and potential damage to thin features. For NADCAP-certified production, the Almen intensity on the drawing is the binding specification.\"\n            }\n        },\n        {\n            \"@type\": \"Question\",\n            \"name\": \"Can shot peening compensate for internal porosity in SLM metal AM parts?\",\n            \"acceptedAnswer\": {\n                \"@type\": \"Answer\",\n                \"text\": \"Shot peening improves surface fatigue resistance but cannot address internal porosity. Conventional peening introduces compressive residual stress only in a shallow surface layer (0.1 to 0.5 mm depth). Internal pores and lack-of-fusion defects deeper than this zone remain unchanged and continue to initiate fatigue cracks under high stress amplitudes. For SLM parts with significant internal porosity, HIP (hot isostatic pressing) is the correct process for porosity closure. The full fatigue optimisation workflow for critical SLM metal AM parts is: HIP (porosity) + heat treatment + blasting + shot peening (surface CRS). Shot peening alone without HIP is insufficient when significant internal porosity is present.\"\n            }\n        },\n        {\n            \"@type\": \"Question\",\n            \"name\": \"What media should be used for shot peening Inconel 718 AM parts?\",\n            \"acceptedAnswer\": {\n                \"@type\": \"Answer\",\n                \"text\": \"Conditioned carbon steel shot (SAE J441) at S110 to S230 sizes is standard for shot peening Inconel 718 AM parts. Steel shot provides the high density and hardness needed for effective peening of this hard nickel superalloy at HRC 40 to 48 after aging. Glass beads at equivalent Almen intensity require significantly higher pressure and produce less effective CRS in Inconel 718. For NADCAP-compliant Inconel aerospace parts, steel shot with documented Almen strip tests and full process records is the standard workflow.\"\n            }\n        },\n        {\n            \"@type\": \"Question\",\n            \"name\": \"How does residual stress from SLM processing affect the shot peening outcome?\",\n            \"acceptedAnswer\": {\n                \"@type\": \"Answer\",\n                \"text\": \"SLM parts are manufactured with tensile residual stress in the as-built surface layer, typically 200 to 800 MPa tensile in titanium and steels, resulting from the thermal gradient between the newly solidified surface and cooler underlying material. This tensile stress adds to applied tensile stress during cyclic loading, reducing the fatigue threshold. Shot peening directly reverses this condition: compressive residual stress introduced by peening (typically 500 to 1200 MPa CRS at the surface for optimised parameters) converts the as-built tensile state to strongly compressive. This combination of eliminating as-built tensile stress AND introducing beneficial CRS explains why shot peening improvements in AM parts often exceed those seen in conventionally manufactured parts.\"\n            }\n        },\n        {\n            \"@type\": \"Question\",\n            \"name\": \"Is laser shock peening (LSP) better than conventional shot peening for AM parts?\",\n            \"acceptedAnswer\": {\n                \"@type\": \"Answer\",\n                \"text\": \"Laser shock peening introduces compressive residual stress to greater depth (1 to 3 mm) than conventional shot peening (0.1 to 0.5 mm) and produces a smoother surface. LSP is used for the most critical aerospace titanium and nickel alloy components where maximum fatigue benefit is required. However, LSP costs 10 to 50 times more per part than conventional shot peening and has much slower throughput. For most metal AM production, conventional shot peening with zirconia or steel shot delivers adequate fatigue improvement at a fraction of LSP cost. LSP is reserved for the highest-criticality components where part value and life-criticality justify the process cost.\"\n            }\n        },\n        {\n            \"@type\": \"Question\",\n            \"name\": \"Does shot peening change the dimensional tolerances of SLM parts?\",\n            \"acceptedAnswer\": {\n                \"@type\": \"Answer\",\n                \"text\": \"Yes \\u2014 shot peening introduces a slight dimensional change through the compressive stress layer, manifesting as a very small expansion of the peened surface. For typical SLM parts with wall thickness above 5 mm and standard Almen A peening (0.008 to 0.020 inch arc height), dimensional change from shot peening is below 0.03 mm. For thin-walled structures below 2 mm wall and intensive peening, distortion can be 0.05 to 0.15 mm. Critical-tolerance features such as precision bores, mating faces, and thread forms should be masked from shot peening or machined to final dimension after peening to compensate for peening-induced dimensional change.\"\n            }\n        }\n    ]\n}<\/script>\n<span class=\"hlh-3dp-c10-badge\">Technical Guide<\/span>\n<h1>Shot Peening 3D Printed Metal Parts: Improving Fatigue Life with Compressive Residual Stress<\/h1>\n<div class=\"hlh-3dp-c10-meta\">\n  <span>Updated July 2026<\/span>\n  <span>By Jiangsu Henglihong Technology Co., Ltd.<\/span>\n  <span>~5,000 words \u00b7 11 min read<\/span>\n<\/div>\n<p class=\"hlh-3dp-c10-intro\">Fatigue failure \u2014 crack initiation and propagation under cyclic loading \u2014 is the dominant failure mode for metal structures in aerospace, automotive, and medical applications. Metal 3D printed parts from SLM and DMLS processes are particularly susceptible because the as-built state combines surface roughness, tensile residual stress from rapid solidification, and potential sub-surface porosity. Shot peening directly addresses the most critical of these factors: it introduces compressive residual stress (CRS) at the part surface, reversing the as-built tensile state and significantly raising the fatigue threshold. This guide covers the mechanics of shot peening, Almen intensity specification, media selection for AM alloys, and the documentation requirements for NADCAP-certified peening operations.<\/p>\n<div class=\"hlh-3dp-c10-back\">&#8617; Part of our complete resource: <a href=\"https:\/\/hlh-js.com\/resource\/blog\/abrasive-blasting-3d-printed-parts-surface-finishing-guide\/\" target=\"_blank\" rel=\"noopener noreferrer\">Abrasive Blasting for 3D Printed Parts: The Complete Post-Processing and Surface Finishing Guide<\/a><\/div>\n<nav class=\"hlh-3dp-c10-toc\"><p class=\"hlh-3dp-c10-toc-title\">Table of Contents<\/p>\n<ol>\n<li><a href=\"#c10-s1\">The Fatigue Problem with Metal 3D Printed Parts<\/a><\/li>\n<li><a href=\"#c10-s2\">What Is Shot Peening? Mechanism and Physics<\/a><\/li>\n<li><a href=\"#c10-s3\">Residual Stress in SLM\/DMLS Parts: The Starting Condition<\/a><\/li>\n<li><a href=\"#c10-s4\">Shot Peening vs Bead Blasting: Key Differences<\/a><\/li>\n<li><a href=\"#c10-s5\">Fatigue Life Improvements: Data by Alloy<\/a><\/li>\n<li><a href=\"#c10-s6\">Shot Peening Media for AM Parts<\/a><\/li>\n<li><a href=\"#c10-s7\">Almen Intensity and Coverage Specification<\/a><\/li>\n<li><a href=\"#c10-s8\">Shot Peening Protocols by Alloy<\/a><\/li>\n<li><a href=\"#c10-s9\">Documentation and NADCAP Qualification<\/a><\/li>\n<li><a href=\"#c10-faq\">Preguntas frecuentes<\/a><\/li>\n<\/ol><\/nav>\n\n<a id=\"c10-s1\"><\/a>\n<h2>1. The Fatigue Problem with Metal 3D Printed Parts<\/h2>\n<p>Fatigue is the progressive, localised structural damage that occurs when a material is subjected to cyclic loading. Almost all structural failures in aerospace and automotive applications are fatigue failures, initiated at surface defects or stress concentrations that are far below the material&#8217;s static tensile strength.<\/p>\n<p>SLM and DMLS metal AM parts are more susceptible to fatigue failure than wrought equivalents for three compounding reasons:<\/p>\n<ul>\n<li><strong>Surface roughness:<\/strong> As-built Ra 8\u201320 \u00b5m creates notch-like surface asperities that act as stress concentrators. Studies on SLM Ti-6Al-4V show stress concentration factors (Kt) of 1.5\u20133.0 at layer-line ridges and partially melted powder attachments, significantly reducing fatigue strength versus smooth polished specimens.<\/li>\n<li><strong>Tensile residual stress:<\/strong> The rapid heating and cooling cycles of the SLM laser leave the part surface in tensile residual stress (typically +200 to +800 MPa in titanium and steel SLM parts). Tensile surface stress adds to applied tensile stress during cyclic loading, reducing the cyclic stress amplitude at which cracks initiate.<\/li>\n<li><strong>Sub-surface porosity:<\/strong> SLM parts with even 0.1\u20131% porosity contain voids that act as internal stress concentrators. Surface cracks grow faster when a sub-surface pore is encountered, causing earlier failure than in fully dense wrought parts.<\/li>\n<\/ul>\n<p>Shot peening addresses surface roughness (via pre-peen blast) and tensile residual stress (by converting it to compressive) \u2014 the two surface-related factors. Sub-surface porosity requires HIP for effective mitigation.<\/p>\n\n<div class=\"hlh-3dp-c10-stats\">\n<div class=\"hlh-3dp-c10-stat\"><div class=\"sv\">25\u201365%<\/div><div class=\"sl\">Fatigue strength improvement \u2014 SLM Ti-6Al-4V after shot peening<\/div><\/div>\n<div class=\"hlh-3dp-c10-stat\"><div class=\"sv\">20\u201350%<\/div><div class=\"sl\">Fatigue strength improvement \u2014 LPBF Inconel 718<\/div><\/div>\n<div class=\"hlh-3dp-c10-stat\"><div class=\"sv\">0.1\u20130.5 mm<\/div><div class=\"sl\">Depth of compressive residual stress from conventional peening<\/div><\/div>\n<div class=\"hlh-3dp-c10-stat\"><div class=\"sv\">\u2212500 to \u22121200 MPa<\/div><div class=\"sl\">Typical surface CRS after shot peening of AM alloys<\/div><\/div>\n<\/div>\n\n<a id=\"c10-s2\"><\/a>\n<h2>2. What Is Shot Peening? Mechanism and Physics<\/h2>\n<p>Shot peening propels hard, spherical particles at a metal surface under controlled conditions. Each spherical impact creates a Hertzian contact stress field that locally exceeds the material&#8217;s yield strength at and just below the surface. The surface layers deform plastically, expanding laterally. The surrounding elastic material resists this expansion \u2014 placing the deformed layer in a state of biaxial compressive residual stress.<\/p>\n<p>The result is a work-hardened surface layer in compression, extending from the surface to a depth determined by the shot size, hardness, and impact energy. This compressive layer produces two fatigue-beneficial effects:<\/p>\n<ol>\n<li><strong>Crack closure:<\/strong> Compressive residual stress holds cracks closed during the tensile loading phase, reducing the effective stress intensity range (\u0394K) and slowing crack propagation rate per cycle.<\/li>\n<li><strong>Crack initiation retardation:<\/strong> Compressive surface stress raises the cyclic stress amplitude needed to initiate a fatigue crack from surface defects, effectively increasing the fatigue endurance limit.<\/li>\n<\/ol>\n<p>The CRS introduced by shot peening is a permanent microstructural feature, not a surface coating. It remains effective throughout the part&#8217;s service life as long as the surface layer is not removed by wear, machining, or corrosion.<\/p>\n\n<a id=\"c10-s3\"><\/a>\n<h2>3. Residual Stress in SLM\/DMLS Parts: The Starting Condition<\/h2>\n<p>Unlike conventionally manufactured parts (wrought, forged, machined), which typically have near-neutral or mildly compressive residual stress, as-built SLM\/DMLS parts have a well-documented tensile residual stress state at and near the surface. This arises from the SLM process physics: the laser creates a localised melt pool that solidifies rapidly, contracting on cooling against the surrounding cooler solid. The constrained contraction leaves the surface layers in tension.<\/p>\n<p>X-ray diffraction (XRD) measurements on as-built SLM Ti-6Al-4V and 316L consistently show surface residual stresses of +200 to +800 MPa tensile \u2014 a significant fraction of the material&#8217;s tensile strength. This tensile starting condition explains why as-built SLM parts show fatigue strengths well below wrought equivalents: the surface is already pre-loaded in tension before any cyclic load is applied.<\/p>\n<p>Shot peening reverses this state. The CRS introduced (typically converting +400 MPa tensile to \u2212700 MPa compressive, for example) represents a biaxial stress swing of over 1 GPa at the surface \u2014 which is the fundamental reason why shot peening improvements in AM parts often exceed those seen in wrought parts with neutral starting residual stress.<\/p>\n\n<a id=\"c10-s4\"><\/a>\n<h2>4. Shot Peening vs Bead Blasting: Key Differences<\/h2>\n<div class=\"hlh-3dp-c10-tw\">\n<table>\n<thead><tr><th>Par\u00e1metro<\/th><th>Bead Blasting<\/th><th>Granallado<\/th><\/tr><\/thead>\n<tbody>\n<tr><td>Primary purpose<\/td><td>Surface cleaning, Ra reduction, matte finish<\/td><td>Compressive residual stress induction, fatigue life<\/td><\/tr>\n<tr><td>Media<\/td><td>Fine glass beads (100\u2013250 mesh)<\/td><td>Steel shot, zirconia, ceramic (larger, denser)<\/td><\/tr>\n<tr><td>Process control<\/td><td>Pressure, standoff, coverage (qualitative)<\/td><td>Almen intensity specification (quantitative)<\/td><\/tr>\n<tr><td>Intensity measurement<\/td><td>Not required<\/td><td>Almen arc height (SAE J442) mandatory<\/td><\/tr>\n<tr><td>Cobertura<\/td><td>95\u2013100% (visual)<\/td><td>98\u2013100% minimum (quantified by saturation curve)<\/td><\/tr>\n<tr><td>Surface Ra after process<\/td><td>Decreases 50\u201380% from as-built<\/td><td>Increases slightly vs pre-peen blast surface<\/td><\/tr>\n<tr><td>Regulatory specification<\/td><td>No standard required<\/td><td>AMS 2430, AMS 2432, MIL-S-13165<\/td><\/tr>\n<tr><td>NADCAP required<\/td><td>Not always<\/td><td>Yes \u2014 for certified aerospace parts<\/td><\/tr>\n<\/tbody><\/table><\/div>\n\n<a id=\"c10-s5\"><\/a>\n<h2>5. Fatigue Life Improvements: Data by Alloy<\/h2>\n<div class=\"hlh-3dp-c10-tw\">\n<table>\n<thead><tr><th>AM Alloy \/ Process<\/th><th>Starting Condition<\/th><th>Peening Media<\/th><th>Fatigue Strength Improvement<\/th><\/tr><\/thead>\n<tbody>\n<tr><td>SLM Ti-6Al-4V<\/td><td>As-built + bead blast<\/td><td>Glass beads \/ ZrO\u2082<\/td><td>25\u201365% improvement at 10\u2077 cycles<\/td><\/tr>\n<tr><td>SLM Ti-6Al-4V<\/td><td>HIP + anneal + blast<\/td><td>ZrO\u2082 \/ glass beads<\/td><td>15\u201335% additional over HIP+anneal baseline<\/td><\/tr>\n<tr><td>LPBF Inconel 718<\/td><td>As-built + bead blast<\/td><td>Steel shot S110\u2013S170<\/td><td>20\u201350%<\/td><\/tr>\n<tr><td>SLM 316L SS<\/td><td>As-built + bead blast<\/td><td>Glass beads or ceramic<\/td><td>15\u201340%<\/td><\/tr>\n<tr><td>SLM AlSi10Mg<\/td><td>As-built + bead blast<\/td><td>Glass beads 80\u2013120 mesh<\/td><td>10\u201330%<\/td><\/tr>\n<tr><td>SLM 17-4PH SS<\/td><td>Bead blast<\/td><td>Steel shot S110<\/td><td>20\u201345%<\/td><\/tr>\n<\/tbody><\/table><\/div>\n\n<div class=\"hlh-3dp-c10-note\"><div class=\"nl\">Data Note<\/div><p>Values represent improvement in high-cycle fatigue strength (stress amplitude at 10\u2077 cycles) vs as-built + bead blast condition. Absolute fatigue values depend on geometry, loading mode, and stress ratio. Commission alloy- and geometry-specific fatigue testing for production qualification of critical AM components.<\/p><\/div>\n\n<a id=\"c10-s6\"><\/a>\n<h2>6. Shot Peening Media for AM Parts<\/h2>\n<h3>Steel Shot (S-type)<\/h3>\n<p>Conditioned cast steel shot (SAE J441, SAE J1173) is the standard peening media for carbon steel, alloy steel, and nickel superalloy AM parts. S110 (0.28 mm) and S170 (0.43 mm) are the most commonly used sizes for AM \u2014 smaller than conventional industrial peening sizes because AM parts typically have complex geometry and thin features that are sensitive to over-peening with larger shot. Steel shot is not suitable for titanium or stainless steel due to iron contamination risk.<\/p>\n<h3>Glass Beads (High-Intensity Grade)<\/h3>\n<p>Glass beads at higher pressures (70\u201390 psi) with 80\u2013120 mesh sizes can achieve moderate Almen intensities on softer AM alloys such as AlSi10Mg. Glass beads are the only cost-effective iron-free option for peening titanium AM parts when Almen intensity requirements are within the achievable range. For titanium parts requiring higher Almen intensities than glass beads can deliver, zirconia shot is specified.<\/p>\n<h3>Zirconia Shot (ZrO\u2082)<\/h3>\n<p>Zirconia shot is the premium peening media for titanium and other alloys requiring iron-free peening at higher intensities. ZrO\u2082 density (3.85 g\/cm\u00b3) is approximately 1.5\u00d7 that of glass (2.5 g\/cm\u00b3), providing significantly more impact energy per particle at equivalent velocity. Media cost is 5\u201310\u00d7 glass beads, but media life is 10\u201330\u00d7 longer. Zirconia is mandatory for NADCAP-compliant peening of titanium aerospace AM parts when glass beads cannot meet the Almen intensity specification.<\/p>\n<h3>Cuentas de cer\u00e1mica<\/h3>\n<p>Ceramic shot (aluminium silicate or zirconia-silicate, Mohs 7) is intermediate between glass beads and zirconia in density and peening effectiveness. Used for titanium and stainless steel when contamination risk precludes steel shot but the intensity requirement exceeds glass bead capability. Ceramic shot is more durable than glass beads (3\u201310\u00d7 life) and less expensive than zirconia.<\/p>\n\n<a id=\"c10-s7\"><\/a>\n<h2>7. Almen Intensity and Coverage Specification<\/h2>\n<h3>Almen Test Strips<\/h3>\n<p>Almen strips are spring steel test specimens (dimensions and material per SAE J442) used to quantify shot peening intensity. A strip is mounted in a standard holder and exposed to the peening process under the same conditions as the production part. The arc height of the deformed strip \u2014 measured in thousandths of an inch \u2014 is the Almen intensity specification. Three strip types are defined by thickness:<\/p>\n<ul>\n<li><strong>N strip (0.031 in):<\/strong> Very gentle peening; for thin-section AM parts with wall thickness below 2 mm<\/li>\n<li><strong>A strip (0.051 in):<\/strong> Standard for most AM applications; most common specification range<\/li>\n<li><strong>C strip (0.094 in):<\/strong> Heavy peening for thick-section parts; rarely used for typical AM wall thicknesses<\/li>\n<\/ul>\n<h3>Cobertura<\/h3>\n<p>Coverage is the percentage of the target surface that has been struck by at least one shot particle. 100% coverage \u2014 defined as the point where the entire surface shows overlapping dimple marks under 10\u00d7 magnification \u2014 is the baseline for effective peening. In production, 98\u2013100% coverage is the accepted specification range. Coverage is quantified by saturation curve: the relationship between exposure time and Almen arc height at constant parameters. The saturation point (doubling exposure time increases arc height by less than 10%) establishes the minimum exposure for 100% coverage.<\/p>\n\n<a id=\"c10-s8\"><\/a>\n<h2>8. Shot Peening Protocols by Alloy<\/h2>\n<div class=\"hlh-3dp-c10-tw\">\n<table>\n<thead><tr><th>AM Alloy<\/th><th>Pre-Peen Step<\/th><th>Peening Media<\/th><th>Almen Intensity<\/th><th>Cobertura<\/th><th>Post-Peen<\/th><\/tr><\/thead>\n<tbody>\n<tr><td>Ti-6Al-4V (aerospace)<\/td><td>Glass bead blast to Ra \u2264 3.2 \u00b5m<\/td><td>ZrO\u2082 Z150\u2013Z300<\/td><td>A 0.012\u20130.020 in<\/td><td>100%<\/td><td>Inspect per AMS 2430<\/td><\/tr>\n<tr><td>Ti-6Al-4V (medical)<\/td><td>Glass bead blast to Ra 1.5\u20133.5 \u00b5m<\/td><td>Glass beads or ZrO\u2082<\/td><td>N 0.006\u20130.012 in<\/td><td>98\u2013100%<\/td><td>Ferroxyl test; Ra measurement<\/td><\/tr>\n<tr><td>Inconel 718\/625<\/td><td>Glass bead or Al\u2082O\u2083 blast<\/td><td>Steel shot S110\u2013S170<\/td><td>A 0.010\u20130.020 in<\/td><td>100%<\/td><td>Inspect per AMS 2430<\/td><\/tr>\n<tr><td>316L SS<\/td><td>Glass bead blast<\/td><td>Glass beads or ceramic<\/td><td>A 0.008\u20130.016 in<\/td><td>98\u2013100%<\/td><td>Ferroxyl test; passivation<\/td><\/tr>\n<tr><td>AlSi10Mg<\/td><td>Glass bead blast<\/td><td>Glass beads 80\u2013120 mesh<\/td><td>N 0.006\u20130.012 in<\/td><td>98\u2013100%<\/td><td>Ra measurement; inspect<\/td><\/tr>\n<tr><td>Maraging Steel<\/td><td>Glass bead or Al\u2082O\u2083 blast<\/td><td>Steel shot S110\u2013S170<\/td><td>A 0.012\u20130.022 in<\/td><td>100%<\/td><td>Inspect; machine if required<\/td><\/tr>\n<\/tbody><\/table><\/div>\n\n<a id=\"c10-s9\"><\/a>\n<h2>9. Documentation and NADCAP Qualification<\/h2>\n<p>Shot peening is classified as a Special Process under AS9100 and requires NADCAP accreditation for aerospace supply chain use. Key documentation requirements for NADCAP-compliant shot peening of AM parts:<\/p>\n<ul>\n<li><strong>Process specification:<\/strong> AMS 2430 (Conventional) or AMS 2432 (Computer-Monitored) \u2014 called out on the part drawing<\/li>\n<li><strong>Almen strip test records:<\/strong> Strip type, batch, initial curvature, post-peen arc height, gauge calibration certificate, operator, date, run number<\/li>\n<li><strong>Media certification:<\/strong> Chemical composition, hardness, sieve distribution per SAE J441\/J1173, batch number, supplier CoC<\/li>\n<li><strong>Equipment calibration:<\/strong> Air pressure gauge, Almen gauge, nozzle condition records<\/li>\n<li><strong>Operator qualification:<\/strong> Training records, certification to applicable standard<\/li>\n<li><strong>First Article Inspection (FAI):<\/strong> Per AS9102 \u2014 saturation curve data, coverage verification, Almen records form part of the peening FAI package<\/li>\n<\/ul>\n<p>For detailed aerospace AM surface standards beyond shot peening, see: <a href=\"https:\/\/hlh-js.com\/resource\/blog\/abrasive-blasting-for-aerospace-additive-manufacturing-parts-surface-standards-media-selection-and-compliance\/\" target=\"_blank\" rel=\"noopener noreferrer\">Abrasive Blasting for Aerospace Additive Manufacturing Parts: Surface Standards, Media Selection, and Compliance<\/a>. For the pre-peen surface preparation, see: <a href=\"https:\/\/hlh-js.com\/resource\/blog\/improving-ra-and-rz-on-3d-printed-parts-how-abrasive-blasting-reduces-surface-roughness\/\" target=\"_blank\" rel=\"noopener noreferrer\">Improving Ra and Rz on 3D Printed Parts<\/a>.<\/p>\n\n<a id=\"c10-faq\"><\/a>\n<h2>Preguntas frecuentes<\/h2>\n<div class=\"hlh-3dp-c10-faq\"><details class=\"hlh-3dp-c10-fi\"><summary>What is the difference between shot peening and bead blasting?<\/summary><div class=\"hlh-3dp-c10-fa\"><p>Both use spherical media propelled at a surface, but differ fundamentally in purpose and control. Bead blasting is a surface conditioning and cleaning process \u2014 fine glass beads at material-matched pressures reduce Ra, remove oxide, and create a uniform matte finish. No intensity specification is required. Shot peening is a precision engineering process \u2014 harder, denser media at intensities measured with Almen test strips introduce a specific level of compressive residual stress at a quantified depth. Shot peening is always specified by Almen intensity, coverage percentage, and media type; bead blasting is specified by media mesh size and pressure only. In aerospace production, the two are sequential: bead blasting normalises the surface to the pre-peen Ra, then shot peening applies the Almen-specified intensity.<\/p><\/div><\/details>\n<details class=\"hlh-3dp-c10-fi\"><summary>What Almen intensity should I specify for shot peening SLM Ti-6Al-4V?<\/summary><div class=\"hlh-3dp-c10-fa\"><p>For SLM Ti-6Al-4V, typical Almen A intensities range from 0.008 to 0.015 inch arc height for thin sections (wall thickness below 3 mm) and 0.012 to 0.025 inch for heavier sections. These are broad guidelines; the specific Almen intensity for a production part must come from a fatigue optimisation study or from the design stress analysis. Higher intensity introduces deeper CRS but also higher surface Ra and greater cold-working, which can reduce ductility in thin walls. The optimum balances CRS depth against surface roughness increase and potential damage to thin features. For NADCAP-certified production, the Almen intensity on the drawing is the binding specification.<\/p><\/div><\/details>\n<details class=\"hlh-3dp-c10-fi\"><summary>Can shot peening compensate for internal porosity in SLM metal AM parts?<\/summary><div class=\"hlh-3dp-c10-fa\"><p>Shot peening improves surface fatigue resistance but cannot address internal porosity. Conventional peening introduces compressive residual stress only in a shallow surface layer (0.1 to 0.5 mm depth). Internal pores and lack-of-fusion defects deeper than this zone remain unchanged and continue to initiate fatigue cracks under high stress amplitudes. For SLM parts with significant internal porosity, HIP (hot isostatic pressing) is the correct process for porosity closure. The full fatigue optimisation workflow for critical SLM metal AM parts is: HIP (porosity) + heat treatment + blasting + shot peening (surface CRS). Shot peening alone without HIP is insufficient when significant internal porosity is present.<\/p><\/div><\/details>\n<details class=\"hlh-3dp-c10-fi\"><summary>What media should be used for shot peening Inconel 718 AM parts?<\/summary><div class=\"hlh-3dp-c10-fa\"><p>Conditioned carbon steel shot (SAE J441) at S110 to S230 sizes is standard for shot peening Inconel 718 AM parts. Steel shot provides the high density and hardness needed for effective peening of this hard nickel superalloy at HRC 40 to 48 after aging. Glass beads at equivalent Almen intensity require significantly higher pressure and produce less effective CRS in Inconel 718. For NADCAP-compliant Inconel aerospace parts, steel shot with documented Almen strip tests and full process records is the standard workflow.<\/p><\/div><\/details>\n<details class=\"hlh-3dp-c10-fi\"><summary>How does residual stress from SLM processing affect the shot peening outcome?<\/summary><div class=\"hlh-3dp-c10-fa\"><p>SLM parts are manufactured with tensile residual stress in the as-built surface layer, typically 200 to 800 MPa tensile in titanium and steels, resulting from the thermal gradient between the newly solidified surface and cooler underlying material. This tensile stress adds to applied tensile stress during cyclic loading, reducing the fatigue threshold. Shot peening directly reverses this condition: compressive residual stress introduced by peening (typically 500 to 1200 MPa CRS at the surface for optimised parameters) converts the as-built tensile state to strongly compressive. This combination of eliminating as-built tensile stress AND introducing beneficial CRS explains why shot peening improvements in AM parts often exceed those seen in conventionally manufactured parts.<\/p><\/div><\/details>\n<details class=\"hlh-3dp-c10-fi\"><summary>Is laser shock peening (LSP) better than conventional shot peening for AM parts?<\/summary><div class=\"hlh-3dp-c10-fa\"><p>Laser shock peening introduces compressive residual stress to greater depth (1 to 3 mm) than conventional shot peening (0.1 to 0.5 mm) and produces a smoother surface. LSP is used for the most critical aerospace titanium and nickel alloy components where maximum fatigue benefit is required. However, LSP costs 10 to 50 times more per part than conventional shot peening and has much slower throughput. For most metal AM production, conventional shot peening with zirconia or steel shot delivers adequate fatigue improvement at a fraction of LSP cost. LSP is reserved for the highest-criticality components where part value and life-criticality justify the process cost.<\/p><\/div><\/details>\n<details class=\"hlh-3dp-c10-fi\"><summary>Does shot peening change the dimensional tolerances of SLM parts?<\/summary><div class=\"hlh-3dp-c10-fa\"><p>Yes \u2014 shot peening introduces a slight dimensional change through the compressive stress layer, manifesting as a very small expansion of the peened surface. For typical SLM parts with wall thickness above 5 mm and standard Almen A peening (0.008 to 0.020 inch arc height), dimensional change from shot peening is below 0.03 mm. For thin-walled structures below 2 mm wall and intensive peening, distortion can be 0.05 to 0.15 mm. Critical-tolerance features such as precision bores, mating faces, and thread forms should be masked from shot peening or machined to final dimension after peening to compensate for peening-induced dimensional change.<\/p><\/div><\/details>\n<\/div>\n<div class=\"hlh-3dp-c10-cta\">\n  <h2>Source Shot Peening Media for Metal AM Parts<\/h2>\n  <p>Jiangsu Henglihong Technology Co., Ltd. manufactures steel shot (S110\u2013S230), glass beads, and zirconia shot for shot peening AM components \u2014 all available with full SAE J441\/J1173 batch certification for NADCAP-compliant operations. Contact our team for Almen intensity guidance and media CoC support.<\/p>\n  <a class=\"hlh-3dp-c10-btn\" href=\"https:\/\/hlh-js.com\/contact\/\" target=\"_blank\" rel=\"noopener noreferrer\">Contact Our Technical Team<\/a>\n<\/div>\n<hr class=\"hlh-3dp-c10-div\">\n<p style=\"font-size:.8rem;color:#9ca3af;margin:0;\">Published July 2026 by Jiangsu Henglihong Technology Co., Ltd. \u2014 Specialists in industrial abrasive blasting media for additive manufacturing post-processing.<\/p>\n<\/div>","protected":false},"excerpt":{"rendered":"<p>Technical Guide Shot Peening 3D Printed Metal Parts: Improving Fatigue  [&#8230;]<\/p>","protected":false},"author":1,"featured_media":13752,"comment_status":"closed","ping_status":"open","sticky":false,"template":"","format":"standard","meta":{"footnotes":""},"categories":[62,175,138],"tags":[],"class_list":["post-13733","post","type-post","status-publish","format-standard","has-post-thumbnail","hentry","category-blog","category-industry","category-resource"],"_links":{"self":[{"href":"https:\/\/hlh-js.com\/es\/wp-json\/wp\/v2\/posts\/13733","targetHints":{"allow":["GET"]}}],"collection":[{"href":"https:\/\/hlh-js.com\/es\/wp-json\/wp\/v2\/posts"}],"about":[{"href":"https:\/\/hlh-js.com\/es\/wp-json\/wp\/v2\/types\/post"}],"author":[{"embeddable":true,"href":"https:\/\/hlh-js.com\/es\/wp-json\/wp\/v2\/users\/1"}],"replies":[{"embeddable":true,"href":"https:\/\/hlh-js.com\/es\/wp-json\/wp\/v2\/comments?post=13733"}],"version-history":[{"count":2,"href":"https:\/\/hlh-js.com\/es\/wp-json\/wp\/v2\/posts\/13733\/revisions"}],"predecessor-version":[{"id":13735,"href":"https:\/\/hlh-js.com\/es\/wp-json\/wp\/v2\/posts\/13733\/revisions\/13735"}],"wp:featuredmedia":[{"embeddable":true,"href":"https:\/\/hlh-js.com\/es\/wp-json\/wp\/v2\/media\/13752"}],"wp:attachment":[{"href":"https:\/\/hlh-js.com\/es\/wp-json\/wp\/v2\/media?parent=13733"}],"wp:term":[{"taxonomy":"category","embeddable":true,"href":"https:\/\/hlh-js.com\/es\/wp-json\/wp\/v2\/categories?post=13733"},{"taxonomy":"post_tag","embeddable":true,"href":"https:\/\/hlh-js.com\/es\/wp-json\/wp\/v2\/tags?post=13733"}],"curies":[{"name":"wp","href":"https:\/\/api.w.org\/{rel}","templated":true}]}}